The micro-solution electrochemical method to evaluate rebar corrosion in reinforced concrete structures

---

منبع:

Construction and Building Materials 151 (2017) 607–614

---

نویسنده:

Yuwan Tian a,b, Chaofang Dong a,⇑, Xuequn Cheng a, Yingqi Wana, Gui Wang b, Kui Xiao a, Xiaogang Li a

---

چکیده انگلیسی:

An electrochemical method by submersing the HRB400 rebar specimen in simulated micro pore solution (47.125 lL) is proposed to rapidly evaluate the corrosion rate of HRB400 in concrete. The results show that the corrosion rate of HRB400 in micro-solution is about five times lower than that in bulk solution. The reason for this difference is the anodic polarization caused by the higher concentration of dissolved iron ions in micro-solution. There is a small relational dispersed degree of corrosion rate measured by the optimized electrochemical cell in micro-solution and the real site studies.

---

چکیده فارسی:

یک روش الکتروشیمیایی با پوشاندن نمونه های آرماتور HRB400 در محلول شبیه سازی شده (47.125 میکرو لیتر) به منظور ارزیابی سریع نرخ خوردگی HRB400 در بتن ارائه شده است. نتایج نشان می دهد که نرخ خوردگی HRB400 در ریز محلول حدود پنج برابر کمتر از محیط محلولی است. دلیل این تفاوت، ایجاد قطب مثبت است که با تمرکز بیشتر یون های آهن حل نشده در ریز محلول رخ می دهد. مقدار ناچیزی پراکندگی نسبی در نتایج نرخ خوردگی میان سلول الکتروشیمیایی بهینه شده و مطالعات میدانی مشاهده شده است.

---

---

---

---

حجم فایل: 1760 کیلوبایت

---

قیمت: 28000 تومان    22400 تومان (20 % تخفیف)

---

توضیحات اضافی: نظر

---

---

---