  • High strain rate micro-compression for crystal plasticity constitutive law parameters identification High strain rate micro-compression for crystal plasticity constitutive law parameters identification
    High strain rate micro-compression for crystal plasticity constitutive law parameters identification

    سال انتشار:

    2020


    عنوان انگلیسی مقاله:

    High strain rate micro-compression for crystal plasticity constitutive law parameters identification


    ترجمه فارسی عنوان مقاله:

    میزان فشار بالا فشرده سازی میکرو برای شناسایی پارامترهای قانون سازنده انعطاف پذیری کریستال


    منبع:

    Sciencedirect - Elsevier - Materials & Design, 193 (2020) 108789: doi:10:1016/j:matdes:2020:108789


    نویسنده:

    S. Breumier a,⁎, S. Sao-Joao a, A. Villani a, M. Lévesque b, G. Kermouche a


    چکیده انگلیسی:

    Microcompression tests were performed on single crystal copper micropillars at 10−2 s−1 and 102 s−1 in the [100], [110] and [111] orientations, to provide inputs for crystal plasticity strain rate sensitive parameters inverse identification. The identification procedure used full pillar geometry finite element simulations. An identifiability indicator based on the cost functions hessian matrix approximate close to the minimum was used to assess the uniqueness and stability of the identified coefficients. Experimental microcompression tests displayed a strain rate sensitive behaviour in the [100] crystal orientation. The [110] and [111] orientations were less sensitive and were not used for identification. Stress-strain curve sensitivity plots revealed that the higher the strain rate, the better the sensitivity. This was attributed to high strain rates concentration in the shear bands as the strain rate increases. Identification on experimental data well represented the single crystal strain rate sensitivity in the [100] orientations. A unique solution was found using only a single orientation.
    Keywords: Micropillar compression | Crystal plasticity finite element | Inverse identification | Identifiability analysis


    سطح: متوسط
    تعداد صفحات فایل pdf انگلیسی: 17
    حجم فایل: 3076 کیلوبایت

    قیمت: رایگان


    توضیحات اضافی:




اگر این مقاله را پسندیدید آن را در شبکه های اجتماعی به اشتراک بگذارید (برای به اشتراک گذاری بر روی ایکن های زیر کلیک کنید)

تعداد نظرات : 0

الزامی
الزامی
الزامی
rss مقالات ترجمه شده rss مقالات انگلیسی rss کتاب های انگلیسی rss مقالات آموزشی
logo-samandehi