    Effect of graphite and Mn3O4 on clay-bonded SiC ceramics for the production of electrically conductive heatable filter

    سال انتشار:

    2021


    عنوان انگلیسی مقاله:

    Effect of graphite and Mn3O4 on clay-bonded SiC ceramics for the production of electrically conductive heatable filter


    ترجمه فارسی عنوان مقاله:

    اثر گرافیت و Mn3O4 بر سرامیک های SiC پیوند خورده با خاک رس برای تولید فیلتر قابل گرمایش رسانای الکتریکی


    منبع:

    ScienceDirect- Elsevier- Ceramics International, 47 (2021) 23045-23052: doi:10:1016/j:ceramint:2021:05:019


    نویسنده:

    Syed Zaighum Abbas Bukhari


    چکیده انگلیسی:

    Electrically conductive porous SiC ceramics are attracting substantial attention due to their application in heatable filters, vacuum chuck, and semiconductor processing parts, etc. The main problem is their high processing cost. Ideal candidates from an engineering ceramic perspective will be mechanically durable and have the required electrical properties with sufficiently low fabrication costs. To decrease the sintering temperature, kaolin has been added, but it tended to render the material an insulator. Graphite was used to effectively decrease the electrical resistivity. Additionally, manganese oxide was used to decrease the quantity of kaolin (the component that leads to an insulator material after sintering) and decrease the electrical resistivity while maintaining the mechanical properties. In our study, we found that SiC with 35% kaolin, 20% graphite and 10% manganese oxide can produce samples with 6.5 × 10− 1 Ω cm electrical resistivity and 43.5 MPa flexural strength at a low sintering temperature of 1200 ◦C.
    Keywords: SiC | Mullite | Electrical resistivity | Mechanical properties | Manganese oxide


    سطح: متوسط
    تعداد صفحات فایل pdf انگلیسی: 8
    حجم فایل: 8704 کیلوبایت

    قیمت: رایگان


    توضیحات اضافی:




اگر این مقاله را پسندیدید آن را در شبکه های اجتماعی به اشتراک بگذارید (برای به اشتراک گذاری بر روی ایکن های زیر کلیک کنید)

تعداد نظرات : 0

الزامی
الزامی
الزامی
rss مقالات ترجمه شده rss مقالات انگلیسی rss کتاب های انگلیسی rss مقالات آموزشی
logo-samandehi